SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Asia Pacific)

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PC-siloxane copolymer in special metallic colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.

Physical Properties	Metric	English	Comments
Specific Gravity	1.18 g/cc	1.18 g/cc	ASTM D792
Density	1.18 g/cc	0.0426 lb/in³	ISO 1183
Moisture Absorption	0.0900 %	0.0900 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	0.12 %	0.12 %	ISO 62
Linear Mold Shrinkage, Flow	0.0040 - 0.0080 cm/cm	0.0040 - 0.0080 in/in	on Tensile Bar; SABIC Method
	0.0040 - 0.0080 cm/cm @Thickness 3.20 mm	0.0040 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0040 - 0.0080 cm/cm @Thickness 3.20 mm	0.0040 - 0.0080 in/in @Thickness 0.126 in	SABIC Method
Melt Flow	10 g/10 min @Load 1.20 kg, Temperature 300 °C	10 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238
Melt Index of Compound	9.0 g/10 min @Load 1.20 kg, Temperature 300 °C	9.0 g/10 min @Load 2.65 lb, Temperature 572 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	54.0 MPa	7830 psi	50 mm/min; ISO 527
	56.0 MPa	8120 psi	Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield	57.0 MPa	8270 psi	50 mm/min; ISO 527
	58.0 MPa	8410 psi	Type I, 50 mm/min; ASTM D638
Elongation at Break	105 %	105 %	50 mm/min; ISO 527
	110 %	110 %	Type I, 50 mm/min; ASTM D638
Elongation at Yield	5.6 %	5.6 %	50 mm/min; ISO 527
	5.9 %	5.9 %	Type I, 50 mm/min; ASTM D638
Tensile Modulus	2.26 GPa	328 ksi	50 mm/min; ASTM D638
	2.32 GPa	336 ksi	1 mm/min; ISO 527
Flexural Yield Strength	86.0 MPa	12500 psi	1.3 mm/min, 50 mm span; ASTM D790
	89.0 MPa	12900 psi	2 mm/min; ISO 178
Flexural Modulus	2.17 GPa	315 ksi	2 mm/min; ISO 178
	2.27 GPa	329 ksi	1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched	6.10 J/cm	11.4 ft-lb/in	ASTM D256
	2.46 J/cm @Temperature -30.0 °C	4.61 ft-lb/in @Temperature -22.0 °F	ASTM D256
Izod Impact, Notched (ISO)	35.0 kJ/m²	16.7 ft-lb/in²	80104; ISO 180/1A
	14.0 kJ/m² @Temperature -30.0 °C	6.66 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Charpy Impact, Notched	1.60 J/cm²	7.61 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	61.0 J @Temperature 23.0 °C	45.0 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	71.5 µm/m-°C @Temperature -40.0 - 95.0 °C	39.7 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
	71.5 µm/m-°C @Temperature 23.0 - 80.0 °C	39.7 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
CTE, linear, Transverse to Flow	79.3 µm/m-°C @Temperature -40.0 - 95.0 °C	44.1 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E 831
	79.3 µm/m-°C @Temperature 23.0 - 80.0 °C	44.1 µin/in-°F @Temperature 73.4 - 176 °F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	120 °C	248 °F	Flatw 80104 sp=64mm; ISO 75/Af
	122 °C @Thickness 3.20 mm	252 °F @Thickness 0.126 in	unannealed; ASTM D648
Vicat Softening Point	141 °C	286 °F	Rate B/50; ASTM D1525
	141 °C	286 °F	Rate B/50; ISO 306
	143 °C	289 °F	Rate B/120; ISO 306

Descriptive Properties	Value	Comments
Ball Pressure Test, 75°C +/- 2°C	PASS	IEC 60695-10-2