SABIC Innovative Plastics Lexan® FXE144H PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXE144H PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FXE144H is a Lexan PC Translucent Grade in our VisualFX Portfolio. It is part of Energy family, which includes Illuminate, Glass, and Flame effects. Grade was developed to meet the Aesthetic Differentiation requirements of today´s Customers. Color package may effect properties, Application testing reccomended.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on tensile bar; SABIC Method |
| 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
11 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| 11 g/10 min @Load 1.20 kg, Temperature 300 °C |
11 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | Type I, 50 mm/min; ASTM D 638 |
| 70.0 MPa | 10200 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D 638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 110 % | 110 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.34 GPa | 339 ksi | 5 mm/min; ASTM D 638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 32.04 J/cm @Temperature 23.0 °C |
60.02 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.30 J/cm² @Temperature 23.0 °C |
34.7 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 64.0 J @Temperature 23.0 °C |
47.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.3 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.1 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 71.2 µm/m-°C @Temperature 23.0 - 80.0 °C |
39.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 71.2 µm/m-°C @Temperature 23.0 - 80.0 °C |
39.6 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate B/50; ISO 306 |
| 142 °C | 288 °F | Rate B/120; ISO 306 | |
| 154 °C | 309 °F | Rate B/50; ASTM D 1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Omnia Plastica PVDF Kynar
- Kureha KF Polymer 1300 PVDF Homopolymer
- SABIC Innovative Plastics Ultem HATX100 PEI+PCE
- SABIC Innovative Plastics Valox® VAC3003 PBT (Asia Pacific)
- Techmer ES Plastiblend® ABS 8002
- A. Schulman POLYTROPE™ TPP 408 Blow Molding Grade Olefinic Thermoplastic Elastomer
- 3M Dyneon™ FC 2121 Fluoroelastomer
- Total PSI 975E Polystyrene
- HP Alloys Alloy 718, 5% Cold Worked
- Chevron Phillips 7105DKT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved