SABIC Innovative Plastics Lexan® FXE1413T PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® FXE1413T PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.35 % | 0.35 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.12 % @Temperature 23.0 °C |
0.12 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
9.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 10 g/10 min @Load 1.20 kg, Temperature 300 °C |
10 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 124.9 % | 124.9 % | 50 mm/min; ISO 527 |
| 131.4 % | 131.4 % | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527 |
| 5.8 % | 5.8 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.21 GPa | 321 ksi | 50 mm/min; ASTM D 638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 94.0 MPa | 13600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.15 GPa | 312 ksi | 2 mm/min; ISO 178 |
| 2.21 GPa | 321 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 7.95 J/cm @Temperature -30.0 °C |
14.9 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 8.90 J/cm @Temperature 23.0 °C |
16.7 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 65.0 kJ/m² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Impact Test | 82.0 J @Temperature 23.0 °C |
60.5 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 71.5 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.7 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 71.5 µm/m-°C @Temperature 23.0 - 80.0 °C |
39.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.3 µm/m-°C @Temperature -40.0 - 95.0 °C |
44.1 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 79.3 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 124 °C @Thickness 3.20 mm |
255 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 141 °C | 286 °F | Rate A/50; ASTM D 1525 |
| 141 °C | 286 °F | Rate B/50; ISO 306 | |
| 142 °C | 288 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | pass | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- NYC YT3CP Y2O3 Powder
- Ravago Manufacturing Americas Hylon® N1233HL BK Nylon 6/6
- Huntsman Araldite PZ 3902 Water-Based Adhesive/Coating
- Huntsman MY 0500 Multifunctional Resin
- Mi-Tech Metals CW80 80 Tungsten/20 Copper PM Metal Composite
- SABIC Innovative Plastics NORYL N110S PPE+HIPS (Europe-Africa-Middle East)
- DuPont Teijin Films Melinex® 454 Polyester Film, 92 Gauge
- Asahi Kasei Tenac®-C CF454 Copolymer Polyacetal Resin
- 3M 4492G Double Coated Polyethylene Foam Tape
Copyright © lookpolymers.com All Rights Reserved