SABIC Innovative Plastics Lexan® FR735A Polycarbonate Film, Flame Retardant

Category	Polymer , Film , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Lexan®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Lexan® FR735A Polycarbonate Film, Flame Retardant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Lexan FR735A is a black, one side velvet, one polish flame-retardant polycarbonate film with a UL94 V-0 listing at 0.250 mm. This film has formability, excellent mechanical properties, good dimensional stability at high temperatures and a high flammability rating, making it good for applications such as power supply insulation, disc drive insulation, bus-bar insulation, TV/monitor insulation, PC board insulation, business equipment insulation and has insulation and EMI/RFI shielding when laminated with metal foil.Information provided by SABIC Innovative Plastics

Physical Properties	Metric	English	Comments
Density	1.34 g/cc	0.0484 lb/in³	ASTM D792
Water Absorption	0.28 %	0.28 %	24 hrs; ASTM D570
Surface Tension	36 - 38 dynes/cm	36 - 38 dynes/cm	1st surface; units: Dyne; Dyne Pens
	36 - 38 dynes/cm	36 - 38 dynes/cm	2nd surface; units: Dyne; Dyne Pens

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	75.8 MPa	11000 psi	ASTM D882
Tensile Strength, Yield	74.5 MPa	10800 psi	ASTM D882
Elongation at Break	100 - 160 %	100 - 160 %	ASTM D882
Tensile Modulus	2.19 GPa	318 ksi	ASTM D882
Gardner Impact	14.9 J @Thickness 0.762 mm	11.0 ft-lb @Thickness 0.0300 in	ASTM D3029
Impact Test	12.2 J	9.00 ft-lb	Puncture Resistance, Dynatup; ASTM D3763
Tear Strength	7.27 kN/m	41.5 pli	propogation; ASTM D1922
	251 kN/m	1430 pli	initiation; ASTM D1004

Thermal Properties	Metric	English	Comments
CTE, linear	57.6 µm/m-°C	32.0 µin/in-°F	ASTM E831
Specific Heat Capacity	1.26 J/g-°C	0.301 BTU/lb-°F	ASTM E1269
Thermal Conductivity	0.200 W/m-K	1.39 BTU-in/hr-ft²-°F	ASTM D5470
Deflection Temperature at 1.8 MPa (264 psi)	143.3 °C	289.9 °F	TMA
Vicat Softening Point	175 °C	347 °F	ASTM 1525-00 modified
Brittleness Temperature	-135 °C	-211 °F	ASTM D746
Glass Transition Temp, Tg	153 °C	307 °F	ASTM D3417/D3418
Flammability, UL94	V-0 @Thickness 0.250 - 0.375 mm	V-0 @Thickness 0.00984 - 0.0148 in
	V-0 @Thickness >=0.375 mm	V-0 @Thickness >=0.0148 in
Shrinkage	0.020 % @Temperature 150 °C	0.020 % @Temperature 302 °F	ASTM D1204

Optical Properties	Metric	English	Comments
Gloss	12 %	12 %	over Flat Black min/max @ 60º; ASTM D523-60

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm	1.00e+17 ohm-cm	ASTM D257
Surface Resistivity per Square	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Dielectric Constant	2.8 @Frequency 1.00e+6 Hz	2.8 @Frequency 1.00e+6 Hz	ASTM D150
	2.9 @Frequency 60.0 Hz	2.9 @Frequency 60.0 Hz	ASTM D150
Dielectric Strength	68.0 kV/mm @Temperature 23.0 °C	1730 kV/in @Temperature 73.4 °F	in oil, short time. 0.25mm; ASTM D149-97a Method A
Dissipation Factor	0.0026 @Frequency 60.0 Hz	0.0026 @Frequency 60.0 Hz	ASTM D150
	0.0117 @Frequency 1.00e+6 Hz	0.0117 @Frequency 1.00e+6 Hz	ASTM D150
Arc Resistance	64 sec	64 sec	Tungsten; ASTM D495

Descriptive Properties	Value	Comments
Fold Endurance (folds)	12	MIT; ASTM D2176-69; double, 0.50mm
	27	MIT; ASTM D2176-69; double, 0.25mm
Nominal Gauge Variation (%)	5	0.250 - 0.500mm
Surface Energy	35	2nd surface; ASTM D5946-01
	36	1st surface; ASTM D5946-01