 POLYMER SEARCH

DSM Akulon® XP32-E1 PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade
Manufacturer DSM Engineering Plastics
Trade Name Akulon®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Akulon® XP32-E1 PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film Extrusion, Medium Viscosity, Lubricated, Nucleated
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Vapor Transmission 35.0 g/m²/day

@Temperature 23.0 °C
 2.25 g/100 in²/day

@Temperature 73.4 °F
 at 85% r.h., Film; DIS 15106-1/-3
Oxygen Transmission 1.05 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
 2.67 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
 at 0% r.h., Film; DIS 15105-1/-2
1.55 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
 3.94 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
 at 85% r.h., Film; DIS 15105-1/-2
Viscosity 1.45e+6 cP

@Temperature 260 °C
 1.45e+6 cP

@Temperature 500 °F
 Melt Viscosity; DSM Method
200000 cP

@Shear Rate 1000 1/s,
Temperature 280 °C
 200000 cP

@Shear Rate 1000 1/s,
Temperature 536 °F
250000 cP

@Shear Rate 1000 1/s,
Temperature 260 °C
 250000 cP

@Shear Rate 1000 1/s,
Temperature 500 °F
300000 cP

@Shear Rate 1000 1/s,
Temperature 240 °C
 300000 cP

@Shear Rate 1000 1/s,
Temperature 464 °F
1.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 280 °C
 1.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 536 °F
2.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 260 °C
 2.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 500 °F
3.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 240 °C
 3.00e+6 cP

@Shear Rate 0.100 1/s,
Temperature 464 °F
Viscosity Measurement 2.8
2.8
RSV formic acid, 1g/100ml; DSM Method
Viscosity Test 177 cm³/g
177 cm³/g
Viscosity Number; ISO 307, 1157, 1628
Thickness 50.0 microns
1.97 mil
Film
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 36.0 MPa
5220 psi
parallel; ISO 527-3
Film Elongation at Break, MD 340 %
340 %
parallel; ISO 527-3
Modulus of Elasticity 0.490 GPa
71.1 ksi
Film; DSM-Method, 50mm/min
Coefficient of Friction, Dynamic 0.80
0.80
Film; ISO 8295
Coefficient of Friction, Static 1.4
1.4
Film; ISO 8295
Tear Strength Test 23
23
Trouser Tear Resistance, parallel, Film; ISO 6383-1
Film Tensile Strength at Break, MD 96.0 MPa
13900 psi
parallel; ISO 527-3
Thermal Properties Metric English Comments
CTE, linear 90.0 µm/m-°C
50.0 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 1.55 J/g-°C

@Temperature 23.0 °C
 0.370 BTU/lb-°F

@Temperature 73.4 °F
2.55 J/g-°C

@Temperature 20.0 - 150 °C
 0.609 BTU/lb-°F

@Temperature 68.0 - 302 °F
Optical Properties Metric English Comments
Transmission, Visible 85 %
85 %
Film; DSM Method
Processing Properties Metric English Comments
Processing Temperature 270 °C
518 °F
Extruder Temperature, Film
Die Temperature 270 °C
518 °F
Roll Temperature 110 °C
230 °F
Descriptive Properties Value Comments
Extrusion Type Cast Film
Puncture Resistance 1200 J/m
Film (DSM Method)