EMS-Grivory Grivory® L 25 G nat 6011 PA12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer EMS-Grivory (EMS-CHEMIE)
Trade Name Grivory®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF EMS-Grivory Grivory® L 25 G nat 6011 PA12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Grilamid L 25 G natural 6011 is a high viscosity, lubricated polyamide 12. This product has the following features: Very tastelessHigh toughness, even at low temperaturesGood resistance to weatheringGood chemical resistanceMechanical properties only slightly dependent on relative humiditySignificantly lower water absorption than polyamide 6 Application examples: Grilamid L 25 G natural 6011 is suitable for the manufacture of blown and cast film being mono or coextruded. Grilamid L 25 G natural 6011 is used for artificial sausage casings for precooked sausages and packaging films for deep-frozen goods.Information provided by EMS Grivory
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Water Absorption 1.5 %
1.5 %
ISO 62
Moisture Absorption 0.700 %
0.700 %
ISO 62
Water Vapor Transmission 8.00 g/m²/day
0.515 g/100 in²/day
23°C/85%r.h.; DIS 15106-1/-2
Oxygen Transmission Rate 350 cc/m²/day
22.5 cc/100 in²/day
23°C/0%r.h.; DIS 15105-1/-2
370 cc/m²/day
23.8 cc/100 in²/day
23°C/85%r.h.; DIS 15105-1/-2
Carbon Dioxide Transmission 1500 cc-mm/m²-24hr-atm
3810 cc-mil/100 in²-24hr-atm
23°C/0%r.h.; DIS 15105-1/-2
1600 cc-mm/m²-24hr-atm
4060 cc-mil/100 in²-24hr-atm
23°C/85%r.h.; DIS 15105-1/-2
Melt Flow 20 g/10 min
20 g/10 min
(MVR) [cm³/10min]; ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 35.0 MPa
5080 psi
ISO 527-3
Film Tensile Strength at Yield, TD 35.0 MPa
5080 psi
ISO 527-3
Film Elongation at Break, MD 850 %
850 %
ISO 527-3
Film Elongation at Break, TD 900 %
900 %
ISO 527-3
Film Elongation at Yield, MD 6.0 %
6.0 %
ISO 527-3
Film Elongation at Yield, TD 6.0 %
6.0 %
ISO 527-3
Tensile Modulus 1.10 GPa
160 ksi
conditioned; ISO 527-1/-2
1.60 GPa
232 ksi
dry; ISO 527-1/-2
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
conditioned; ISO 179/1eA
0.700 J/cm²

@Temperature 30.0 °C
3.33 ft-lb/in²

@Temperature 86.0 °F
conditioned; ISO 179/1eU
Tear Strength 20.0 kN/m
114 pli
Trouser Tear resistance MD; ISO 6383-1
25.0 kN/m
143 pli
Trouser Tear resistance TD; ISO 6383-1
Elmendorf Tear Strength MD 1020 g
1020 g
ISO 6383-2
Elmendorf Tear Strength TD 1020 g
1020 g
ISO 6383-2
Film Tensile Strength at Break, MD 80.0 MPa
11600 psi
ISO 527-3
Film Tensile Strength at Break, TD 70.0 MPa
10200 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Optical Properties Metric English Comments
Gloss 150 %
150 %
60°; ISO 2813
Descriptive Properties Value Comments
Food contact EU Requirements
FDA
Form Granules
Gelboflextest [holes/m²], EMS 1300
Packaging Non oriented film
Processing Other Extrusion
Product Attributes High viscosity