SABIC Innovative Plastics LNP Verton UV00ASXS PPA (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Verton UV00ASXS PPA (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* UV00ASXS is a compound based on Polyphthalamide resin containing Long Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 % @Temperature 23.0 °C, Time 86400 sec |
0.40 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec |
0.0017 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 245 MPa | 35500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Flexural Strain, 2 mm/min; ISO 178 | |
| Tensile Modulus | 20.4 GPa | 2960 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 417 MPa | 60500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 17.7 GPa | 2570 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 38.0 kJ/m² @Temperature 23.0 °C |
18.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 297 °C | 567 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Victrex® PEEK 450GL20 Polyetheretherketone, 20% Glass Fibre Reinforced
- Lehmann & Voss LUVOCOM® 19-7950 Polyamide 46, with aramid reinforcement and PTFE, toughness-modified, easy flowing
- Hyosung Topilene B200P PP
- Industrial Laminates/Norplex NP319 Cotton Fabric Base Laminate
- A. Schulman POLYBATCH™ Yellow LL20203/2 Concentrate Based In LDPE
- Crucible Compaction Metals Rene 95 Nickel Based Superalloy
- Chosun Refractories LPCT-17PI Lance Castable
- CMW® ELKONIUM 18 silver, copper, cadmium alloy
- 3M Scotch-Weld™ HP69 Pipe Sealant Anaerobic Adhesives
- Beijing Chemical Industry KAIFA® 301-G20 PBT Resin
Copyright © lookpolymers.com All Rights Reserved