SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing, Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 |
| 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
| 97.0 MPa | 14100 psi | ISO 527 | |
| Elongation at Break | 3.3 % | 3.3 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Tensile Modulus | 6.16 GPa | 893 ksi | 50 mm/min; ASTM D638 |
| 6.92 GPa | 1000 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 137 MPa | 19900 psi | ASTM D790 |
| 151 MPa | 21900 psi | ISO 178 | |
| Flexural Modulus | 5.97 GPa | 866 ksi | ASTM D790 |
| 6.56 GPa | 951 ksi | ISO 178 | |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.67 J/cm | 8.75 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 46.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
26.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 69.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 113 µm/m-°C @Temperature -40.0 - 40.0 °C |
62.8 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Resin Technology Group Fusion 830 General Purpose Fusion Cyanoacrylate
- LG Chemical BM662 ABS, Heat Resistance
- Multibase Multibatch® MP 53663 Sheet Extrusion
- Hexcel® HexPly® M42 180°C (350°F) Curing Epoxy Matrix, 52%/G1177 Glass/Carbon Fiber
- DSM Akulon® K224-G6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond)
- ChevronTexaco Multifak® EP NLGI Grade 2
- ExxonMobil Medium Mobil DTE Oil Named Series
- Addiplast Addilene H 555 Y7 Polypropylene Homopolymer
- Sax Polymers SAXAMID 236F6Q32 Nylon 6.6, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved