SABIC Innovative Plastics LNP VERTON RV00AESC PA 66 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV00AESC PA 66 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV00AESC is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Time 86400 sec |
0.0015 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0043 cm/cm @Time 86400 sec |
0.0043 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 254 MPa | 36800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 17.3 GPa | 2510 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 370 MPa | 53700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 15.6 GPa | 2260 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1A |
| 38.0 kJ/m² @Temperature -40.0 °C |
18.1 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² | 41.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 15.0 J | 11.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
11.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
30.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- PolyOne Syncure™ V0030G RoHS Polyethylene, Crosslinked (XLPE)
- Lanxess Durethan® BKV 30 G H2.0 900051 Nylon 6, 30% Glass Fiber
- Borealis HD822CF Polypropylene
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Carbon Black, N-326 (HS-HAF)
- Covestro Bayflex® 110-50 Polyurethane Elastomeric RIM, 15% Mineral Filled, MDI-based 2-Component Liquid System
- Entec Hypro™ PP-CP0.5/10 Impact Copolymer, Fractional Melt Flow
- Aclo Accutech Polypropylene Homopolymer HP0334M40CL Mica Reinforced Coupled
- Aaron Industries AVPS GP(crystal) 100-1 Virgin Polystyrene - Crystal
- PolyOne Edgetek® PI-20GM/000 L Polyetherimide (PEI), Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved