SABIC Innovative Plastics LNP VERTON RV008ES PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON RV008ES PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* VERTON* RV008ES is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.700 % | 0.700 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0029 cm/cm @Time 86400 sec |
0.0029 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0069 cm/cm @Time 86400 sec |
0.0069 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 206 MPa | 29900 psi | ISO 527 |
| 213 MPa | 30900 psi | ASTM D638 | |
| Tensile Strength, Yield | 207 MPa | 30000 psi | ISO 527 |
| 213 MPa | 30900 psi | ASTM D638 | |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| 1.9 % | 1.9 % | ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | ASTM D638 |
| 2.0 % | 2.0 % | ISO 527 | |
| Tensile Modulus | 13.21 GPa | 1916 ksi | 1 mm/min; ISO 527 |
| 13.78 GPa | 1999 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 301 MPa | 43700 psi | ISO 178 |
| 303 MPa | 43900 psi | ASTM D790 | |
| Flexural Modulus | 11.72 GPa | 1700 ksi | ASTM D790 |
| 12.0 GPa | 1740 ksi | ISO 178 | |
| Izod Impact, Notched | 2.13 J/cm | 3.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.28 J/cm | 23.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 61.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 27.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
15.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 252 °C @Thickness 3.20 mm |
486 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JA612EA Polyvinyl Chloride, Flexible (PVC, Flexible)
- MV Labs PT160 K2Pt(CN)4 Potassium tetracyanoplatinate(II)
- Global TPP-120 20% Talc Filled Polypropylene
- Multibase Multi-Flex® A 8030 TPE Thermoplastic Elastomer
- SABIC Innovative Plastics LNP Thermocomp OF008E PPS
- Samsung Cheil Industries Infino® WP-1098 PC/ABS, Unreinforced
- Solvay MACKAMIDE® CD-81 Surfactant
- Dow Corning SILASTIC® LSR 9390-60 PARTS A&B
- Clariant PA223 Nylon 6, Impact Modified, Heat Stabilized, Lubricated
- SABIC Innovative Plastics ULTEM 1000 PEI (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved