SABIC Innovative Plastics LNP VERTON MV00AS PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON MV00AS PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP VERTON* MV00AS is a compound based on Polypropylene resin containing Long Glass. Added features of this material include: Chemically Coupled, heat stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 209 MPa | 30300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 147 x 10-8 mm³/N-M | 73.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 34.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
18.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
25.6 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers XP23-566-1 PVC
- SABIC Innovative Plastics Lexan® 203R PC (Asia Pacific)
- SABIC HP0722N Low Density Polyethylene for Blown Film
- SABIC Innovative Plastics LNP STAT-KON PE002Z PA 6
- ExxonMobil Enable™ 35-05HH Metallocene Polyethylene Resin (European Grade)
- ChevronTexaco Starplex® Moly MPGM 2
- Hippe PC Polycarbonate
- Premix Premi-Glas® 1282-32 VE Glass Reinforced Vinyl Ester SMC (discontinued **)
- DuPont Performance Polymers Kalrez® 3018 FFKM Perfluoroelastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved