ExxonMobil LD 105.BR Very High Clarity Packaging Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil LD 105.BR Very High Clarity Packaging Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: LD 105 resins are homopolymer packaging film resins designed for applications requiring outstanding clarity with good stiffness. These resins can be processed in either blown or cast film equipment. In blown film equipment LD 105.30 can be drawn down to 1.0 mil gauge.Availability: Latin America, North America and South America Additive: Antiblock: 1000 ppmSlip: 750 ppmThermal Stabilizer: YesApplications: Blend PartnerBread BagsDisplay Packaging FilmFood packagingForm Fill and Seal PackagingFreezer FilmHigh Clarity FilmHigh Quality LaminationLamination FilmLaundry FilmLight Duty Shrink FilmProduce BagsSalad BagsTextile Packaging Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ExxonMobil Method
Thickness	38.1 microns	1.50 mil
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Antiblock Level	1000 ppm	1000 ppm
Slip Level	750 ppm	750 ppm

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	11.0 MPa	1600 psi	ASTM D882
Film Tensile Strength at Yield, TD	11.0 MPa	1600 psi	ASTM D882
Film Elongation at Break, MD	210 %	210 %	ASTM D882
Film Elongation at Break, TD	570 %	570 %	ASTM D882
Puncture Energy	0.757 J	0.558 ft-lb	ExxonMobil Method
Elmendorf Tear Strength MD	350 g	350 g	ASTM D1922
Elmendorf Tear Strength TD	190 g	190 g	ASTM D1922
Dart Drop Test	100 g	0.221 lb	ASTM D1709
Film Tensile Strength at Break, MD	24.9 MPa	3610 psi	ASTM D882
Film Tensile Strength at Break, TD	21.4 MPa	3100 psi	ASTM D882
1% Secant Modulus, MD	214 MPa	31000 psi	ASTM D882
1% Secant Modulus, TD	255 MPa	37000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	111 °C	232 °F	Peak Melting Temperature; ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	5.2 %	5.2 %	ASTM D1003
Gloss	76 %	76 %	45°; ASTM D2457
Transmission, Visible	90 %	90 %	clear; thickness not quantified

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer