Arlon 55146R028 Silicone Rubber/Fiberglass Laminate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 55146R028 Silicone Rubber/Fiberglass Laminate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Interleave: 3 mil PE; Side 2: uncured silicone rubber; Substrate: 162 fiberglass; Side 1: cured silicone rubber
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | silicone property; Arlon SQA-TMS-024 |
| Thickness | 102 microns | 4.00 mil | side 1; Arlon SQA-TMS-003 |
| 165 microns | 6.50 mil | side 2; Arlon SQA-TMS-003 | |
| 483 microns | 19.0 mil | substrate; Arlon SQA-TMS-003 | |
| 749 microns | 29.5 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | silicone property; ASTM D2240 |
| Tensile Strength, Ultimate | 5.52 MPa | 800 psi | silicone property; ASTM D412 |
| Elongation at Break | 225 % | 225 % | silicone property; ASTM D412 |
| Adhesive Bond Strength | 0.0490 MPa | 7.10 psi | Arlon SQA-TMS-011 |
| Tear Strength | 15.8 kN/m | 90.0 pli | Die B; silicone property; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 200 °C | 392 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 23.2 kV/mm | 590 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
|
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 50.0 psi, Temperature 250 °F |
||
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red |
Users viewing this material also viewed the following:
- Lucite International Elvacite ® 2552 Acrylic Resin
- Saint-Gobain CHR® SG06-10(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Stir SpA POROCELL Z 559 AT (PVC)
- Samsung Cheil Industries Infino® HX-4300G PPA, Glass Filled
- Hexcel® IM6 Carbon Fiber (12,000 Filaments)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 40 PHR Carbon Black, N-330 (HAF)
- 3M Scotch-Weld™ 3798LM Low Melt Adhesive
- 3M 9593 Double Coated Tapes with Adhesive 350
- BASF Capron® 8232G HS 25% Glass-Filled Nylon 6 (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved