SABIC Innovative Plastics LNP Thermocomp WB008 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp WB008 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* WB008 is a compound based on Thermoplastic Polyester (PBT) containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.66 g/cc
1.66 g/cc
ASTM D 792
Density 1.66 g/cc
0.0600 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.51 %
0.51 %
23°C / 50% RH; ISO 62
0.42 %

@Time 86400 sec
 0.42 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.010 - 0.030 cm/cm

@Time 86400 sec
 0.010 - 0.030 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 47.0 MPa
6820 psi
5 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 47.0 MPa
6820 psi
5 mm/min; ISO 527
Elongation at Break 1.7 %
1.7 %
Type I, 5 mm/min; ASTM D 638
1.7 %
1.7 %
5 mm/min; ISO 527
Elongation at Yield 1.6 %
1.6 %
5 mm/min; ISO 527
Tensile Modulus 4.86 GPa
705 ksi
1 mm/min; ISO 527
5.07 GPa
735 ksi
50 mm/min; ASTM D 638
Flexural Strength 79.0 MPa
11500 psi
1.3 mm/min, 50 mm span; ASTM D 790
82.0 MPa
11900 psi
ISO 178
Flexural Yield Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 4.62 GPa
670 ksi
1.3 mm/min, 50 mm span; ASTM D 790
4.66 GPa
676 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.320 J/cm

@Temperature 23.0 °C
 0.599 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 2.88 J/cm

@Temperature 23.0 °C
 5.40 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature 23.0 °C
 0.952 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 16.0 kJ/m²

@Temperature 23.0 °C
 7.61 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
4.00 J

@Temperature 23.0 °C
 2.95 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 39.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 67.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 37.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
189 °C

@Thickness 3.20 mm
 372 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
 253 °F

@Thickness 0.126 in
 unannealed; ASTM D 648