SABIC Innovative Plastics LNP Thermocomp RF008U PA 66 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP Thermocomp RF008U PA 66 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* RF008U is a compound based on PA 66 resin containing Glass Fiber. Added features include; UV-Stabilized, Easy Molding.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.

Physical Properties	Metric	English	Comments
Density	1.46 g/cc	0.0527 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	189 MPa	27400 psi	5 mm/min; ISO 527
Elongation at Break	2.3 %	2.3 %	5 mm/min; ISO 527
Flexural Strength	276 MPa	40000 psi	2 mm/min; ISO 178
Flexural Modulus	11.0 GPa	1600 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	14.0 kJ/mÂ² @Temperature 23.0 Â°C	6.66 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	70.0 kJ/mÂ² @Temperature 23.0 Â°C	33.3 ft-lb/inÂ² @Temperature 73.4 Â°F	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	27.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	15.0 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	258 Â°C	496 Â°F	Flatw 80104 sp=64mm; ISO 75/Af