Chevron Phillips Vytek™ V205C3 Enhanced LLDPE Blown Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips Vytek™ V205C3 Enhanced LLDPE Blown Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: slip, antiblock, and processing aid additivesCharacteristics: excellent dart impact, hot-tack and heat seal properties, good drawdown, can be used straight or blendedApplications: thick or thin film applications where excellent toughness and abuse resistance, hot-tack and heat seal properties are requiredNatural ColorSlip: 1000 ppmAntiblock: 3000 ppm.Recommended processing conditions: 6.35 cm extruder. 24:1 screw L/D ratio. 0.203 cm die opening. Melt temperature 232°C. Blow up ratio 2.5:1. Output rate 8.0 lb/hr/in die cir.Hot-Tack Initiation Temperature: 96°CUltimate Hot-Tack Strength: 3 NHeat Seal Initiation Temperature at 0.5 lb.: 99°CUltimate Heat Seal Strength: 12.8 N.Film properties based on thickness of 0.0318 mm.Information provided by Chevron Phillips Chemical Company.

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³	ASTM D4883
Melt Flow	0.50 g/10 min	0.50 g/10 min	Condition E; ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	730 %	730 %	ASTM D882
Secant Modulus, MD	0.220 GPa	31.9 ksi	ASTM D882
Secant Modulus, TD	0.250 GPa	36.3 ksi	ASTM D882
Coefficient of Friction	0.10	0.10	ASTM D1894
Elmendorf Tear Strength, MD	17.7 g/micron	450 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	30.3 g/micron	770 g/mil	ASTM D1922
Dart Drop	19.5 g/micron	495 g/mil	F-50 at 26 in.; ASTM D1709
Dart Drop Test	620 g	1.37 lb	F-50 at 26 in.; ASTM D1709
Film Tensile Strength at Break, MD	55.9 MPa	8110 psi	ASTM D882
Film Tensile Strength at Break, TD	39.2 MPa	5690 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	18 %	18 %	ASTM D2457
Gloss	47 %	47 %	45°. ASTM D 2457
	75 %	75 %	60°. ASTM D 2457

Processing Properties	Metric	English	Comments
Melt Temperature	235 - 240 °C	455 - 464 °F