SABIC Innovative Plastics LNP Thermocomp MF006S PP (Asia Pacific)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MF006S PP (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* MF006S is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D 792 |
| 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm @Time 86400 sec |
0.0065 in/in @Time 24.0 hour |
ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0098 cm/cm @Time 86400 sec |
0.0098 in/in @Time 24.0 hour |
ISO 294 |
| 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | ISO 527 |
| 81.0 MPa | 11700 psi | ASTM D 638 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D 638 |
| 3.0 % | 3.0 % | ISO 527 | |
| Tensile Modulus | 9.12 GPa | 1320 ksi | 1 mm/min; ISO 527 |
| 14.47 GPa | 2099 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D 790 |
| 135 MPa | 19600 psi | ISO 178 | |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D 790 |
| 6.80 GPa | 986 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 6.03 J/cm @Temperature 23.0 °C |
11.3 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 69.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 44.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
24.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 45.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
25.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 161 °C | 322 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 157 °C @Thickness 3.20 mm |
315 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 133 °C @Thickness 3.20 mm |
271 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1106-8087/BL Polyether imide, unreinforced, laser markable
- Lushan PJ-1 Polypropylene Compounds for Steel Pipe Top Coats
- Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, DRY
- SABIC Innovative Plastics NORYL GTX GTX973 PPE+PA
- DuPont Performance Polymers Hytrel® 40CB Polyester Elastomer TPC-ET (Unverified Data**)
- Asahi Kasei Tenac® 9054 Homopolymer Acetal Resin
- Resinlab® EP1238 Acrylic / Epoxy Hybrid Adhesive
- Multibase Multibatch® MP 52577 Sheet Extrusion
- Polyram RamTal PM1013 Acetal, General Purpose
Copyright © lookpolymers.com All Rights Reserved