SABIC Innovative Plastics LNP Thermocomp LC006E PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp LC006E PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* LC006E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| 1.41 g/cc | 0.0509 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | 23°C / 50% RH; ISO 62 |
| 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0011 cm/cm @Time 86400 sec |
0.0011 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0077 cm/cm @Time 86400 sec |
0.0077 in/in @Time 24.0 hour |
ISO 294 |
| 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 227 MPa | 32900 psi | ASTM D 638 |
| 228 MPa | 33100 psi | ISO 527 | |
| Elongation at Break | 1.0 % | 1.0 % | ISO 527 |
| 1.3 % | 1.3 % | ASTM D 638 | |
| Tensile Modulus | 24.56 GPa | 3562 ksi | 1 mm/min; ISO 527 |
| 24.95 GPa | 3619 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 340 MPa | 49300 psi | ASTM D 790 |
| 340 MPa | 49300 psi | ISO 178 | |
| Flexural Modulus | 21.64 GPa | 3139 ksi | ASTM D 790 |
| 21.65 GPa | 3140 ksi | ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.32 J/cm @Temperature 23.0 °C |
8.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 18.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
10.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 34.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 34.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
18.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 300 °C @Thickness 3.20 mm |
572 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Network Polymers MS 125 Styrene Methyl Methacrylate Terpolymer
- Noltex Soarnol® AT4403 Ethylene Vinyl Alcohol Copolymer
- Aardvark Polymers AARTEL® 800AM Rotational Molding Resin
- MetalTek C86200 Med. Tensile Manganese Bronze
- Lanxess Durethan® BKV 115 H2.0 DUS008 000000 Nylon 6, 15% Glass Fiber
- Techmer ES HiFill® PA6 G/C50 A240 BK 50% Glass/Ceramic Filled
- ExxonMobil Mobil Aero HFS
- Dow Corning SILASTIC® 37087-V SILICONE RUBBER NATURAL
- CP-Polymer-Technik Wellamid® 6000 GV 25 HWCP 25% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved