SABIC Innovative Plastics LNP THERMOCOMP MF742XXH PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF742XXH PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MF742XXH is a compound based on Polypropylene resin containing Glass Fiber and proprietary antimicrobial additives. This product is best suited for touch surfaces in healthcare applications. Added features include: low antimicrobial performance, high mechanical strength, healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 58.0 MPa | 8410 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.85 GPa | 703 ksi | 1 mm/min; ISO 527 |
| 5.10 GPa | 740 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 87.0 MPa | 12600 psi | ISO 178 |
| Flexural Yield Strength | 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.30 GPa | 624 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.60 GPa | 667 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 161 °C @Thickness 3.20 mm |
322 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 144 °C @Thickness 3.20 mm |
291 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® CL 10 Butene Copolymer Linear Low Density Polyethylene
- Lehmann & Voss LUVOCOM® 1301-0793 PPS, linear, with glass fiber
- IRPC Polimaxx Polene 121PC Styrene Acrylonitrile
- Schott Nextrema® 724-3 Glass Ceramic
- SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP (Asia Pacific)
- Zeon Chemicals Sivic® Z740 Polyblend Nitrile Elastomer
- Covestro Makrolon® GF9002* Polycarbonate, 10% Glass Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- Resinlab® EP1282 Clear Unfilled Electronic Grade Epoxy Encapsulant
- Polyram RamShine PAS703 ASA, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved