SABIC Innovative Plastics LNP Thermocomp GF008 PSU
| Category | Polymer , Thermoplastic , Polysulfone (PSU) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp GF008 PSU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* GF008 is a compound based on Polysulfone resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D 792 |
| 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 108 MPa | 15700 psi | ASTM D 638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D 638 |
| 1.4 % | 1.4 % | ISO 527 | |
| Tensile Modulus | 11.65 GPa | 1690 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 158 MPa | 22900 psi | ASTM D 790 |
| 164 MPa | 23800 psi | ISO 178 | |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ISO 178 |
| 11.7 GPa | 1700 ksi | ASTM D 790 | |
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C |
1.20 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 3.79 J/cm @Temperature 23.0 °C |
7.10 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 176 °C @Thickness 3.20 mm |
349 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- PolyMirae Moplen HF461Y Fiber (Melt-blown) Grade Polypropylene
- Abatron AboCast 8-20/Abocure 8-20 Epoxy (discontinued **)
- Hybrid Plastics CO6U50.02 Nanoreinforced® Cyclic Olefin Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP RVL36 PA 66 (Europe-Africa-Middle East)
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 17 lb
- Stir SpA POROCELL Z 660 ATS (PVC)
- A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate
- DuPont Teijin Films Melinex® ST339 Polyester Film, 1000 Gauge
- Eurostar Starpylen MCR13S PP, 15% Carbon Fiber Filled, Injection Molded
- China Tungsten ZP35 Tungsten Carbide
Copyright © lookpolymers.com All Rights Reserved