SABIC Innovative Plastics LNP Thermocomp DF002L PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp DF002L PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF002L is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Low Extractible.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D 792 |
| 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.21 % | 0.21 % | 23°C / 50% RH; ISO 62 |
| 0.13 % @Time 86400 sec |
0.13 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D 638 |
| 72.0 MPa | 10400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D 638 |
| 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 5.6 % | 5.6 % | 5 mm/min; ISO 527 |
| 6.8 % | 6.8 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 4.2 % | 4.2 % | 5 mm/min; ISO 527 |
| 4.5 % | 4.5 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 3.80 GPa | 551 ksi | 50 mm/min; ASTM D 638 |
| 3.89 GPa | 564 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 3.59 GPa | 521 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 3.60 GPa | 522 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.35 J/cm @Temperature 23.0 °C |
2.53 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 12.27 J/cm @Temperature 23.0 °C |
22.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 82.0 kJ/m² @Temperature 23.0 °C |
39.0 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 23.0 J | 17.0 ft-lb | Multiaxial Impact; ISO 6603 |
| 30.0 J @Temperature 23.0 °C |
22.1 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 147 °C | 297 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 139 °C @Thickness 3.20 mm |
282 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FR2 Modified-PPO, V-1 Flame Retardant
- PolyOne Bergamid™ B700 G20 H UF Polyamide 6 (Nylon 6)
- 3M Dyneon™ Fluorel™ FX-11818 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
- Honeywell ACLAR® 22C (3.00 mil) Copolymer Film (discontinued **)
- 3M Dyneon™ PVDF 1010/0001 Polyvinylidene Fluoride (discontinued **)
- Techmer ES HiFill® PA6 GF43 LE BK 43% Glass Filled
- Polyram PlusTek PD120BK11 Nylon 12 for Extrusion, UV Stabilized
- Dow Corning RD ANTIFOAM EMULSION
- Eurotec® Tecomid® NT40 GR15 NL HS PPA, 15% glass fiber reinforced, heat stabilized, natural
- ArcelorMittal Torque 20-15 Electrical Steel
Copyright © lookpolymers.com All Rights Reserved