Menzolit Menzolit® SMC 0650 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 0650 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 0650 Low pressure SMC for large panels when moulding force becomes critical. Specific moulding pressure < 20 bar. A Special molding procedure is necessary.Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 50.0 MPa @Temperature 22.0 °C |
7250 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 50.0 MPa @Temperature 22.0 °C |
7250 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 133 MPa @Temperature 22.0 °C |
19300 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 7.00 GPa @Temperature 22.0 °C |
1020 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 3.80 GPa | 551 ksi | in plane |
| Charpy Impact, Notched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.0 µm/m-°C | 6.67 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 120 - 150 °C | 248 - 302 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- MV Labs CO735 [Co(C2H8N2)3](NO3)3 Tris(ethylenediamine)cobalt(III) nitrate
- RheTech Products G40P100-04UV 40% Glass Fiber Reinforced Polypropylene, UV Stabilized, White
- Network Polymers NPS 90-0645 Super High Impact Polystyrene
- Flint Hills P9G1Z-047 Polypropylene
- Indium Corp. Indalloy 74 Bismuth-Lead-Tin Solder Alloy
- Kostat ICP-STAT ICD-1005 ABS Sheet
- UBE 5033B Air Blown Nylon 6/66 Film
- 3M Scotchcal™ ElectroCut™ 7725-120 Graphic Film
- 3M Scotch-Weld™ 1751 B/A Epoxy Adhesive
- 3M Dyneon™ Fluorel™ FLS-2650 Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved