SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP WF006L PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* WF006L is a compound based on PBT resin containing 30% Glass Fiber. Added feature of this material is: Low Extractible.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0062 cm/cm @Time 86400 sec |
0.0062 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0134 cm/cm @Time 86400 sec |
0.0134 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 99.0 MPa | 14400 psi | 5 mm/min; ISO 527 |
| 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 50 mm/min; ASTM D638 |
| 12.96 GPa | 1880 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 151 MPa | 21900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.83 GPa | 1140 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.13 GPa | 1320 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.670 J/cm | 1.26 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.57 J/cm | 10.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm |
430 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 205 °C @Thickness 3.20 mm |
401 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nitriflex Nitrigum 50 G Styrene Butadiene Rubber
- Quadrant EPP Nylatron® WP PA (ASTM Product Data Sheet)
- Pau Tai UNISTAB BT-18A Organo Tin Stabilizer
- Lucobit Lucocell® FG3000 Cellulose Asphalt Additive
- SABIC Innovative Plastics LNP THERMOCOMP 67002XXH PBT+PC
- DuPont Performance Polymers Rynite® RE5231 BK533 Polyethylene Terephthalate (PET)
- Arkema Group Rilsan® AESN P302 TL Nylon 12, Flexible Tubing Grade (Conditioned)
- Addiplast Addinyl B2 ZV20 Nylon 6, 20% Glass Filled
Copyright © lookpolymers.com All Rights Reserved