SABIC Innovative Plastics LNP THERMOCOMP UX06032 PPA (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP UX06032 PPA (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* THERMOCOMP* UX06032 is a compound based on Polyphthalamide resin containing Glass Fiber, Flame Retardant. Added features of this material include: Flame Retardant, Non-Brominated & Non-Chlorinated Flame Retardant, Heat Stabilized.

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/inÂ³	ISO 1183
Water Absorption	0.50 % @Time 86400 sec	0.50 % @Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	on Tensile Bar; SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	160 MPa	23200 psi	5 mm/min; ISO 527
Elongation at Break	2.4 %	2.4 %	5 mm/min; ISO 527
Tensile Modulus	11.1 GPa	1610 ksi	1 mm/min; ISO 527
Flexural Strength	220 MPa	31900 psi	2 mm/min; ISO 178
Flexural Modulus	10.2 GPa	1480 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	50.0 kJ/mÂ²	23.8 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	265 Â°C	509 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	UL 94
Glow Wire Test	825 Â°C	1520 Â°F	IEC 60695-2-13
	825 Â°C	1520 Â°F	IEC 60695-2-13
	850 Â°C	1560 Â°F	IEC 60695-2-13
	960 Â°C @Thickness 1.50 mm	1760 Â°F @Thickness 0.0591 in	IEC 60695-2-12

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	IEC 60112