SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP UF006H PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* UF006H is a compound based on Polyphthalamide resin containing 30% Glass Fiber. Added feature of this grade is: Healthcare.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
1.53 g/cc
0.0553 lb/in³
ASTM D792
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0037 cm/cm

@Time 86400 sec
 0.0037 in/in

@Time 24.0 hour
 ISO 294
0.0040 cm/cm

@Time 86400 sec
 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0077 cm/cm

@Time 86400 sec
 0.0077 in/in

@Time 24.0 hour
 ISO 294
0.0080 cm/cm

@Time 86400 sec
 0.0080 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 208 MPa
30200 psi
ISO 527
224 MPa
32500 psi
ASTM D638
Tensile Strength, Yield 208 MPa
30200 psi
ISO 527
224 MPa
32500 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ISO 527
2.2 %
2.2 %
ASTM D638
Elongation at Yield 2.0 %
2.0 %
ISO 527
2.2 %
2.2 %
ASTM D638
Tensile Modulus 12.44 GPa
1804 ksi
1 mm/min; ISO 527
13.1 GPa
1900 ksi
50 mm/min; ASTM D638
Flexural Strength 289 MPa
41900 psi
ASTM D790
294 MPa
42600 psi
ISO 178
Flexural Modulus 11.0 GPa
1600 ksi
ISO 178
11.03 GPa
1600 ksi
ASTM D790
Izod Impact, Notched 1.06 J/cm
1.99 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.83 J/cm
12.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 7.00 J
5.16 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 50.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 28.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
51.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 28.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 28.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 16.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 293 °C
559 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
305 °C

@Thickness 3.20 mm
 581 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 282 °C
540 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
287 °C

@Thickness 3.20 mm
 549 °F

@Thickness 0.126 in
 unannealed; ASTM D648