- Polyram PlusTek PA352M6 Nylon 6.6, 30% Low Friction Mineral Filled
Polyram PlusTek PA352M6 Nylon 6.6, 30% Low Friction Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Mineral Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PA352M6 Nylon 6.6, 30% Low Friction Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% low friction mineral filled polyamide 6.6 lubricated with molybdenum for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | DIN 53479 |
| Water Absorption | 5.5 % | 5.5 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50%RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM-D785 |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ASTM-D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM-D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 220 °C | 428 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 85.0 kV/mm | 2160 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- Gharda Chemicals Gafone™ 3610GM20 Polyethersulfone (PES) (discontinued **)
- LG Chemical TR556 MABS, Transparency, Chemical Resistance
- Gwent Electronic Materials P2121112P1 Acid Vapor Plasma Modified Graphene Nanoplatelets
- Indium Corp. Indalloy 55 Bismuth Solder Alloy
- Schott N-BAK1 Glass
- SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific)
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- DuPont™ Elvax® 3128-1 Ethylene Vinyl Acetate
- Azoty Tarnow™ TARNOFORM KSI POM
Copyright © lookpolymers.com All Rights Reserved