SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP SF008 PA 12.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* SF008 is a compound based on Nylon 12 resin containing 40% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec |
0.0073 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 135 MPa | 19600 psi | ASTM D638 |
| 152 MPa | 22000 psi | ISO 527 | |
| Elongation at Break | 9.0 % | 9.0 % | ISO 527 |
| 10.5 % | 10.5 % | ASTM D638 | |
| Tensile Modulus | 8.27 GPa | 1200 ksi | 50 mm/min; ASTM D638 |
| 8.76 GPa | 1270 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| 213 MPa | 30900 psi | ISO 178 | |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| 9.00 GPa | 1310 ksi | ISO 178 | |
| Izod Impact, Notched | 2.56 J/cm | 4.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.41 J/cm | 27.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm |
349 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 170 °C @Thickness 3.20 mm |
338 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Niche Polymer PPHT40BK Homopolymer PP, 40% Talc Fiber Filled
- SABIC Innovative Plastics LNP KONDUIT PX08322 PA 6 (Europe-Africa-Middle East)
- LG Chemical SEETEC PB270 HDPE
- MetalTek WC 6 Cast UNS J24054 Alloy Steel
- SABIC Innovative Plastics LNP STAT-LOY AF3009 ABS
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Washington Penn High Modulus Polypropylene Homopolymer 40% Glass Filled
- Barlog Plastics KEBAFLEX U A 85 ST B01 natural TPU, Shore A85, natural
- 3M Scotchcal™ 3632-83 Translucent Film
Copyright © lookpolymers.com All Rights Reserved