SABIC Innovative Plastics LNP THERMOCOMP RX08401 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX08401 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX08401 is a compound based on Nylon 66 containing Glass Fiber. Added feature of this grade include: Impact Modified.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.860 % | 0.860 % | 50% RH, 24 hrs; ASTM D570 |
| 1.40 % | 1.40 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 139 MPa | 20200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.43 GPa | 1220 ksi | 1 mm/min; ISO 527 |
| 8.52 GPa | 1240 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 198 MPa | 28700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 206 MPa | 29900 psi | ISO 178 | |
| Flexural Modulus | 7.44 GPa | 1080 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 7.73 GPa | 1120 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.09 J/cm | 9.54 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 253 °C @Thickness 3.20 mm |
487 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 236 °C @Thickness 3.20 mm |
457 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Q7-4720 Dow-Corning Biomedical Grade ETR Elastomer
- Precision Polymer Engineering H70B Epichlorohydrin
- Qualchem Danamid FES Polyamide 6
- Solvay Specialty Polymers Hylar® 301F Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- Lanxess Durethan® AC 30 DUS027 000000 Nylon 66
- SABIC Innovative Plastics LNP Thermocomp MF006ASJ PP
- A. Schulman PP 3490-01G Polypropylene Homopolymer Polypropylene
- American Elements Terbium Oxide Nanopowder
- DuPont Performance Polymers Delrin® 527UV BK701 Acetal (POM) (Unverified Data**)
- 3M 2515 Flat Back Paper Masking Tape
Copyright © lookpolymers.com All Rights Reserved