SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX06421S PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX06421S is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.900 % | 0.900 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | ASTM D638 |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| Tensile Modulus | 9.81 GPa | 1420 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 206 MPa | 29900 psi | ASTM D790 |
| Flexural Modulus | 7.68 GPa | 1110 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.58 J/cm | 14.2 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C @Thickness 3.20 mm |
442 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs YB700 Yb(NO3)3·5H2O Ytterbium nitrate pentahydrate
- SABIC Innovative Plastics Lexan® HP2NR PC (Europe-Africa-Middle East)
- PolyOne Geon™ Vinyl Fittings 210(HR) Polyvinyl Chloride, Rigid (PVC, Rigid)
- Momentive Performance Materials TUFELâ„¢ III 92656 Biocompatible Extrusion Heat Cured Rubber
- Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes
- Universal Wire Works ZA61A (AMS 4350) Magnesium Alloy Filler Metal
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- 3M Dyneon™ PFA 6505TZ Fluoroplastic Granules
Copyright © lookpolymers.com All Rights Reserved