SABIC Innovative Plastics LNP THERMOCOMP RC006 PA6.6 (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC006 PA6.6 (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RC006 is a compound based on PA6.6 resin containing Carbon Fiber. Added features include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ISO 62-1 |
| Water Absorption at Saturation | 4.5 % | 4.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00040 - 0.00080 cm/cm | 0.00040 - 0.00080 in/in | on Tensile Bar; SABIC Method |
| 0.00050 - 0.010 cm/cm | 0.00050 - 0.010 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ISO 2039-2 |
| Tensile Strength at Break | 250 MPa | 36300 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 261 MPa | 37900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 22.0 GPa | 3190 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 360 MPa | 52200 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 360 MPa | 52200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 18.9 GPa | 2740 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -40.0 °C |
2.86 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -20.0 °C |
3.33 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² | 30.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C @Temperature 23.0 - 60.0 °C |
4.44 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 86.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 257 °C | 495 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |
| Vicat Softening Point | 255 °C | 491 °F | Rate B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
UL 94 by SABIC-IP |
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4320 ohm-cm | 4320 ohm-cm | IEC 60093 |
| Surface Resistance | 4320 ohm | 4320 ohm | ROA; IEC 60093 |
| 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Quadrant EPP Monocast® MC 904P Nylon for Pile Driver Pads (ASTM Product Data Sheet)
- Shin-Etsu Silicones X-21-5037 Fluid
- SK Chemicals SKYTHANE® 155D R series Polyurethane
- Sumitomo Bakelite North America E 2748A Short Glass Fiber Reinforced Epoxy
- A. Schulman POLYBATCH™ Blue 4025 Concentrate Based In Polyethylene
- Trelleborg Neoprene® C432 Chloroprene
- Eifeler Coatings Technology ZrCN PVD Coating
- DuPont Performance Polymers Delrin® 520MP NC010 Acetal (POM) (Unverified Data**)
- Aclo Accutech Polypropylene Copolymer CP0437T20L1 Talc Reinforced
Copyright © lookpolymers.com All Rights Reserved