SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP QF0069 PA6.10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* QF0069 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ASTM D792
1.56 g/cc
0.0564 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0029 cm/cm

@Time 86400 sec
 0.0029 in/in

@Time 24.0 hour
 ISO 294
0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0086 cm/cm

@Time 86400 sec
 0.0086 in/in

@Time 24.0 hour
 ISO 294
0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ISO 527
150 MPa
21800 psi
ASTM D638
Tensile Strength, Yield 145 MPa
21000 psi
ISO 527
150 MPa
21800 psi
ASTM D638
Elongation at Break 1.8 %
1.8 %
ISO 527
2.0 %
2.0 %
ASTM D638
Elongation at Yield 1.8 %
1.8 %
ISO 527
2.0 %
2.0 %
ASTM D638
Tensile Modulus 11.02 GPa
1598 ksi
1 mm/min; ISO 527
11.03 GPa
1600 ksi
50 mm/min; ASTM D638
Flexural Strength 197 MPa
28600 psi
ISO 178
199 MPa
28900 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
9.65 GPa
1400 ksi
ASTM D790
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.03 J/cm
11.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
67.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 39.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
40.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 22.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 218 °C
424 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
220 °C

@Thickness 3.20 mm
 428 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
201 °C

@Thickness 3.20 mm
 394 °F

@Thickness 0.126 in
 unannealed; ASTM D648