SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| 1.309 g/cc | 0.04729 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.330 % | 0.330 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0017 - 0.0018 cm/cm @Time 86400 sec |
0.0017 - 0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0098 - 0.0099 cm/cm @Time 86400 sec |
0.0098 - 0.0099 in/in @Time 24.0 hour |
ISO 294 |
| 0.010 cm/cm @Time 86400 sec |
0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| 153 MPa | 22200 psi | ISO 527 | |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| 3.6 % | 3.6 % | ASTM D638 | |
| Tensile Modulus | 8.41 GPa | 1220 ksi | 50 mm/min; ASTM D638 |
| 8.80 GPa | 1280 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 219 MPa | 31800 psi | ISO 178 |
| 250 MPa | 36300 psi | ASTM D790 | |
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 |
| 7.86 GPa | 1140 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.22 J/cm | 2.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.16 J/cm | 20.91 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 71.0 kJ/m² | 33.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 9.00 J | 6.64 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 72.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 72.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 3.20 mm |
405 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- MV Labs ND880 Nd(OH)3·xH2O Neodymium(III) hydroxide hydrate
- Polymax® Maxelast® P1855 TPE, PP Overmold or Standalone use
- Polykemi AB SCANMID 6 B12^ F20 Nylon 6, Glass Fiber Reinforced
- Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA) (Unverified Data**)
- A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- ExxonMobil Label-Lyte™ 50ML580 OPP Film
- Advanced Polymer Alloys Alcryn® 2095 BK Melt Processable Rubber
Copyright © lookpolymers.com All Rights Reserved