SABIC Innovative Plastics LNP THERMOCOMP PX01658 PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PX01658 PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* PX01658 is a compound based on Nylon 6 containing Proprietary Fillers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.750 % | 0.750 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 257 MPa | 37300 psi | Type I, 5 mm/min; ASTM D638 |
| 267 MPa | 38700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 30.91 GPa | 4483 ksi | 1 mm/min; ISO 527 |
| 32.74 GPa | 4749 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 391 MPa | 56700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 393 MPa | 57000 psi | ISO 178 | |
| Flexural Yield Strength | 392 MPa | 56900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 24.7 GPa | 3580 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 25.77 GPa | 3738 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.2 J/cm | 19.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² | 31.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J @Temperature 23.0 °C |
9.59 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
10.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 64.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm |
428 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Synplast™ DOS-N Di (2-ethylhexyl) Sebacate
- Polimeri Europa Eraclene® ML 70 U High Density Polyethylene - Injection Molding
- SABIC Innovative Plastics Noryl V0150BT PPE+HIPS (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East)
- SABIC Innovative Plastics ULTEM 2310F PEI (Europe-Africa-Middle East)
- ELM® SoyGrease™ EP Premium Biodegradable Extreme Pressure Grease, NLGI Grade 3
- DuPont Performance Polymers Crastin® S600F40 BK851 Polybutylene Terephthalate (PBT) (Unverified Data**)&l
- BASF Neopolen® P 9255 0.06 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved