SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OF006 PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OF006 is a compound based on Linear PPS containing 30% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 126 MPa | 18300 psi | 5 mm/min; ISO 527 |
| 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.96 GPa | 1735 ksi | 1 mm/min; ISO 527 |
| 12.1 GPa | 1750 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 170 MPa | 24700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 10.52 GPa | 1526 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.91 J/cm | 7.33 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
12.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
25.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 276 °C @Thickness 3.20 mm |
529 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 261 °C @Thickness 3.20 mm |
502 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® SOL R C2564-T Styrene - Butadiene Copolymer
- MarkeTech Gallium Arsenide Semiconductor Wafer, n-type, Silicon Doped, HB-GF Grown
- Momentive Performance Materials HV 6/600 Heat Cured Rubber - STEAM Resistant
- Techmer ES Luriblend® PA6 TL25 Nylon 6
- Dow 6D43 Polypropylene Random Copolymer Resin
- CMW® ELKONITE® 3042 Silver Tungsten Carbide contact material ASTM B663
- 3M Headlap Roofing Granule (Pittsboro)
- BP Amoco Accpro® 9965 Enhanced Polypropylene (discontinued **)
- Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
Copyright © lookpolymers.com All Rights Reserved