Vyncolit TX10916 Graphite Filled Novolac Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic |
| Manufacturer | Vyncolit N.V., Sumitomo Bakelite |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vyncolit TX10916 Graphite Filled Novolac Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novolac resin based, graphite filled compound used for low friction applications where dimensional stability is required.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 60 |
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Water Absorption | 0.060 % | 0.060 % | ISO 62 |
| Linear Mold Shrinkage | 0.0044 cm/cm | 0.0044 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ISO 527-1 |
| Elongation at Break | 0.47 % | 0.47 % | ISO 527-1 |
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527-1 |
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
| Compressive Strength | 162 MPa | 23500 psi | ISO 604 |
| Charpy Impact Unnotched | 0.290 J/cm² | 1.38 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.130 J/cm² | 0.619 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | TMA |
| CTE, linear, Transverse to Flow | 28.0 µm/m-°C | 15.6 µin/in-°F | TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 166 °C | >= 331 °F | ISO 75 Af |
| Shrinkage | 0.080 % | 0.080 % | Post Shrinkage; ISO 2577 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Molding Method | Compression | |
| Injection | ||
| Transfer |
Users viewing this material also viewed the following:
- Technetics Group Amicon™ PEEK 30% Carbon (Unverified Data**)
- Hogen Duralloy H1W 55 Tungsten/45 Copper PM Metal Composite
- Saint-Gobain CHR® 2300-10R UHMW Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP THERMOCOMP NF0061 PC+ABS (Europe-Africa-Middle East)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR N330 (HAF) Filler
- Borealis HB306MO Polypropylene
- Dalau Dalcon 025 75% Virgin PTFE, 25% Glass Fiber, Blue
- Asahi Kasei Tenac®-C 4520 Copolymer Acetal Resin
- Beijing Chemical Industry KAIFA® 301-G10F PBT Resin
Copyright © lookpolymers.com All Rights Reserved