SABIC Innovative Plastics LNP THERMOCOMP MF002S PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP MF002S PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* MF002S is a compound based on Polypropylene resin containing Glass Fiber. Added features include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ISO 1183 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.1 % | 4.1 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 74.0 MPa | 10700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 68.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
37.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 15.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- LyondellBasell SEQUEL® 1825 Engineered Polyolefin
- Gromax BFG30-EN04B2 Nylon 6 36% Glass Filled (Conditioned)
- Borealis Bormed™ RD804CF Polypropylene Random Copolymer
- Hexcel® AS4C Carbon Fiber (12,000 Filaments)
- A. Schulman POLYFORT™ PP 3153 Homopolymer Polypropylene
- Trelleborg Emerson & Cuming Eccobond® 1962-31 Needle Bonding Epoxy Adhesive
- Axiall 8805 Moldings & Extrusions Flexible PVC
- Aclo Accutech Polypropylene Copolymer CP0437M30CL Mica Reinforced Coupled
- China-Yixing Longly Refractories Alumina Grinding Balls and Lining Bricks Microcrystal Wear-Resistant Alumina Grinding Media (Balls) and Lining Bricks
- Teknor Apex APEX® 3075-H Polyvinyl Chloride, Flexible
Copyright © lookpolymers.com All Rights Reserved