- SABIC Innovative Plastics LNP THERMOCOMP LC008EXQ PEEK
SABIC Innovative Plastics LNP THERMOCOMP LC008EXQ PEEK
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP LC008EXQ PEEK.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* LC008EXQ is a compound based on Polyetheretherketone containing 40% Carbon Fiber. Added features of this grade include: Electrically Conductive, Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0030 cm/cm @Time 86400 sec |
0.0015 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.014 cm/cm @Time 86400 sec |
0.0070 - 0.014 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 321 MPa | 46600 psi | 5 mm/min; ISO 527 |
| 330 MPa | 47900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 40.42 GPa | 5862 ksi | 1 mm/min; ISO 527 |
| 41.48 GPa | 6016 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 460 MPa | 66700 psi | ISO 178 |
| 492 MPa | 71400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 33.82 GPa | 4905 ksi | 2 mm/min; ISO 178 |
| 35.2 GPa | 5110 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Compressive Strength | 215 MPa | 31200 psi | SABIC Method |
| Poissons Ratio | 0.47 | 0.47 | ASTM E 132 |
| Shear Modulus | 5.003 GPa | 725.6 ksi | ASTM C273 |
| Shear Strength | 126 MPa | 18300 psi | ASTM C273 |
| Izod Impact, Notched | 0.820 J/cm | 1.54 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.63 J/cm | 16.2 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 335 °C @Thickness 3.20 mm |
635 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Dow Corning C6-550 LIQUID SILICONE RUBBER KIT
- Eastman Tenite 360E4861316 Cellulose Acetate Propionate, Clear, Trsp
- ExxonMobil Paxon™ AD60-005 Blow Molding Resin
- Diamond Polymers ABS 1000
- DuPont Performance Polymers Zytel® RS LC1600 BK385 Nylon 1010 (Unverified Data**)
- Dymax 912 Strain Relief, Wire and Parts Tacking Adhesive
- C.O.I.M. LARIPUR® LPR6518 Plasticized Ester Polyurethane
- Asahi Kasei Xyron® 300H Modified Polyphenylene Ether
- BASF Ultramid® A3L HP UV BK 23220 PA66 (Dry)
- 3M FM001 Indoor UL Recognized Clear Polyester Overlaminate Label Product
Copyright © lookpolymers.com All Rights Reserved