SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D792
1.49 g/cc
0.0538 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.016 - 0.018 cm/cm

@Time 86400 sec
 0.016 - 0.018 in/in

@Time 24.0 hour
 ASTM D955
0.017 cm/cm

@Time 86400 sec
 0.017 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.015 - 0.017 cm/cm

@Time 86400 sec
 0.015 - 0.017 in/in

@Time 24.0 hour
 ASTM D955
0.016 cm/cm

@Time 86400 sec
 0.016 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 63.0 MPa
9140 psi
ASTM D638
63.0 MPa
9140 psi
ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
ISO 527
66.0 MPa
9570 psi
ASTM D638
Elongation at Break 3.2 %
3.2 %
ISO 527
3.4 %
3.4 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ISO 527
2.2 %
2.2 %
ASTM D638
Tensile Modulus 5.60 GPa
812 ksi
1 mm/min; ISO 527
6.20 GPa
899 ksi
50 mm/min; ASTM D638
Flexural Strength 103 MPa
14900 psi
ASTM D790
105 MPa
15200 psi
ISO 178
Flexural Modulus 4.40 GPa
638 ksi
ISO 178
4.82 GPa
699 ksi
ASTM D790
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.84 J/cm
7.19 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 26.0 kJ/m²
12.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 6.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
112 µm/m-°C

@Temperature -40.0 - 40.0 °C
 62.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 5.40 µm/m-°C

@Temperature -40.0 - 40.0 °C
 3.00 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
60.5 µm/m-°C

@Temperature -40.0 - 40.0 °C
 33.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 162 °C
324 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 148 °C
298 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
155 °C

@Thickness 3.20 mm
 311 °F

@Thickness 0.126 in
 unannealed; ASTM D648