SABIC Innovative Plastics LNP THERMOCOMP JF003E PES
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP JF003E PES.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* JF003E is a compound based on Polyethersulfone resin containing 15% Glass Fiber. Added features of this material include: Easy Molding.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.450 % | 0.450 % | 50% RH, 24 hrs; ASTM D570 |
| 0.900 % | 0.900 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 101 MPa | 14600 psi | 5 mm/min; ISO 527 |
| 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.66 GPa | 821 ksi | 5 mm/min; ASTM D638 |
| 5.66 GPa | 821 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 174 MPa | 25200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 174 MPa | 25200 psi | ISO 178 | |
| Flexural Modulus | 5.33 GPa | 773 ksi | 2 mm/min; ISO 178 |
| 5.68 GPa | 824 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.440 J/cm | 0.824 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
26.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 3.20 mm |
414 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Kuraray HYBRAR® HD2 Thermoplastic Rubber-HDPE Blend
- Techmer ES HiFill® PP 0112 B AM2 Polypropylene
- Teknor Apex MF 588 Polyvinyl Chloride, Flexible Film
- Teknor Apex Monprene® MP-2336UV Thermoplastic Elastomer
- Teknor Apex Monprene® MP-2850E Thermoplastic Elastomer
- Total PPR 3261 Random Copolymer Polypropylene, Extrusion Grade
- Cossa Polimeri ESTADIENE 1030 V0/Ex Flame Retardant ABS
- Fainplast Compounds GS 89/T Flexible PVC, Injection Molding for Transparent Technical Items
- Clariant Renol PA233HT Nylon 6, Improved Processability, Easily Colorable, Highly Toughened
- Goodfellow Audiolloy® Iron 52/Nickel 48 Alloy
Copyright © lookpolymers.com All Rights Reserved