- SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI
SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EF006ER PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* EF006ER is a compound based on Polyetherimide resin containing 30% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0023 cm/cm @Time 86400 sec |
0.0023 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0052 cm/cm @Time 86400 sec |
0.0052 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 154 MPa | 22300 psi | ISO 527 |
| 164 MPa | 23800 psi | ASTM D638 | |
| Elongation at Break | 7.2 % | 7.2 % | ISO 527 |
| 7.3 % | 7.3 % | ASTM D638 | |
| Tensile Modulus | 14.2 GPa | 2060 ksi | 1 mm/min; ISO 527 |
| 22.06 GPa | 3200 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| 250 MPa | 36300 psi | ISO 178 | |
| Flexural Modulus | 10.34 GPa | 1500 ksi | ASTM D790 |
| 11.7 GPa | 1700 ksi | ISO 178 | |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.46 J/cm | 12.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 42.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C | 394 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 325 Ground Alumina
- Pyrotek PTB 2200 Structural Board
- DuPont Performance Polymers Zytel® FG42A NC010 Nylon 66 (Unverified Data**)
- Kennametal Stellite Deloro® 711 PM cast
- Ineos ABS Lustran® 552 Extrusion, Profile/Substrate
- Formosa Plastics Formolene® 6600A Impact Copolymer Polypropylene
- TSE Industries EcoWIND® T211 Filament Winding Polyurethane Resin for Tanks and Pressure Vessels with Thermoplastic Liners
- Brandenburger BL 20/1 GG EP Rotor Blade Material
- Aremco Corr-Paint™ CP4040-S High Temperature Protective Coating Silicone-Polyester
- Arlon 49100R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved