SABIC Innovative Plastics LNP THERMOCOMP DX13354 PC COPOLYMER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX13354 PC COPOLYMER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
DX13354 is 30% glass fiber reinforced, impact modified and LDS functionalized polycarbonate resin. The features include LDS function, high flow, and good ductility.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm @Thickness 3.20 mm |
0.00060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 300 °C |
16 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 1.20 kg, Temperature 300 °C |
13 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 122 MPa | 17700 psi | Type I, 5 mm/min; ASTM D638 |
| 123 MPa | 17800 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 2.4 % | 2.4 % | Type I, 5 mm/min; ASTM D638 |
| 2.4 % | 2.4 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 8.76 GPa | 1270 ksi | 5 mm/min; ASTM D638 |
| 8.84 GPa | 1280 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 171 MPa | 24800 psi | ASTM D790 |
| Flexural Modulus | 8.02 GPa | 1160 ksi | ASTM D790 |
| Izod Impact, Notched | 1.45 J/cm | 2.72 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/2C |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.52 @Frequency 1.00e+9 Hz |
3.52 @Frequency 1.00e+9 Hz |
ASTM D150 |
| Dissipation Factor | 0.014 @Frequency 1.00e+9 Hz |
0.014 @Frequency 1.00e+9 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® XCY480 PC+ABS (Europe-Africa-Middle East)
- Schott G018-053 Dental Glass
- Solvay Specialty Polymers Solef® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF)
- Techmer ES HiFill® PEEK CF40 HF 40% Carbon Filled
- Styron DL 395PA Modified SB
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- Loctite® 4081 Cyanoacrylate Adhesive
- Du-Co Ceramics S-699 Alumina
- Ascend Performance Materials Vydyne® 65A Nylon 66, General Purpose, intermediate viscosity, DAM
Copyright © lookpolymers.com All Rights Reserved