SABIC Innovative Plastics LNP THERMOCOMP CF008 PS
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP CF008 PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* CF008 is a compound based on Polystyrene resin containing 40% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0700 % | 0.0700 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 57.0 MPa | 8270 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.60 % | 0.60 % | 5 mm/min; ISO 527 |
| 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.64 GPa | 1400 ksi | 1 mm/min; ISO 527 |
| 12.78 GPa | 1854 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.32 GPa | 1497 ksi | 2 mm/min; ISO 178 |
| 11.4 GPa | 1650 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 33.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
18.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 95.0 °C @Thickness 3.20 mm |
203 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 89.0 °C @Thickness 3.20 mm |
192 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ MN-818.S001-8000 Polypropylene, Unspecified (PP, Unspecified)
- Permabond LM113 Anaerobic Threadlocker
- Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17510)
- LG Chemical Lupoy 1302HP-09 Polycarbonate Resin
- Techmer ES HiFill® ASA GF15 15% Glass Filled
- Borealis LE0310-99 Polyethylene Thermoplastic Semiconductive Compound
- A. Schulman POLYBATCH™ Bright While LL80250 Concentrate Based In LLDPE
- Brandenburger S 5000 Ablation Material for Aeronautics and Space Aviation
- California Fine Wire Nickel Alloy 180 Copper Nickel Resistance Wire
- SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU
Copyright © lookpolymers.com All Rights Reserved