SABIC Innovative Plastics LNP THERMOCOMP 2F005 ETFE
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2F005 ETFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* 2F005 is a fluoropolymer compound based on ETFE containing 25% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.87 g/cc | 1.87 g/cc | ASTM D792 |
| Density | 1.87 g/cc | 0.0676 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 59.0 MPa | 8560 psi | Type I, 5 mm/min; ASTM D638 |
| 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 5 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| 8.1 % | 8.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.6 % | 6.6 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.67 GPa | 822 ksi | 1 mm/min; ISO 527 |
| 6.19 GPa | 898 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 87.0 MPa | 12600 psi | ISO 178 |
| Flexural Modulus | 5.20 GPa | 754 ksi | 2 mm/min; ISO 178 |
| 5.48 GPa | 795 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.29 J/cm | 9.91 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
35.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C | 450 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 248 °C @Thickness 3.20 mm |
478 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 190 °C @Thickness 3.20 mm |
374 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 3010-50A Thermoplastic Silicone Vulcanizate
- PTS Trimid® N66-100NL Nucleated, Lubricated Nylon 6/6
- Ineos ABS Lustran® 1460, Injection Grade (discontinued **)
- LATI Later 4-V0HF1 PBT, Flame Retardant
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1530A PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP Thermocomp CF004 PS (Europe-Africa-Middle East)
- Techmer ES HiFill® TPX-HTN-03003 A 40% Mineral Filled
- ExxonMobil BB Mobil DTE Oil Double Letter Series
- Azoty Tarnow™ TARNOFORM 500 UV POM
Copyright © lookpolymers.com All Rights Reserved