SABIC Innovative Plastics LNP Stat-kon ZEL34XXC PPE+PS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon ZEL34XXC PPE+PS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* ZEL34XXC is a compound based on PPE+PS Blend resin containing Carbon Fiber, PTFE. Added features include : Electrically Conductive , Internally Lubricated.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00090 cm/cm | 0.00090 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.10 GPa | 1170 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 18.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
10.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 66.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
36.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 110 MEDICAL DEVICES APPROVED (5 Viscosity) Rapid Bonding Adhesive
- DuPont Performance Polymers Rynite® RE15022 NC010 PET (Unverified Data**)
- SABIC Innovative Plastics Lexan® 925 PC
- Lord Adhesives 320 Toughened, High Viscosity SMC, FRP, General Purpose Epoxy Adhesive
- Lucite International Colacryl ® TS1778 Acrylic Solution Resin
- H.C. Starck Pure Molybdenum Plate, PP-22-2
- Teknor Apex Telcar® TL EF-6123 Thermoplastic Elastomer
- Teknor Apex Telcar® TL-2460A Thermoplastic Elastomer
- Solvay Specialty Polymers Algoflon® 35CAR PTFE; Petroleum Coke and Graphite (discontinued **)
Copyright © lookpolymers.com All Rights Reserved