- Polyram RamOfin PPH316G4 Polypropylene, 20% Glass Fiber
Polyram RamOfin PPH316G4 Polypropylene, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPH316G4 Polypropylene, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber reinforced, high heat stabilized polypropylene for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ISO 2577 |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C |
13 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.50 kJ/m² | 4.52 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 289 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- 3M Dyneon™ PVDF 1012/0180 Polyvinylidene Fluoride (discontinued **)
- Fujipoly Industries Sarcon® 25G-Td Thin-Film GR-TD
- Taiwan Sheen Soon Sheenthane® A8915K Film Grade Thermoplastic Polyurethane Elastomer
- A. Schulman POLYBATCH™ Green 300 Concentrate Based In Polyethylene
- Zeon Chemicals Nipol® 1401LG Nitrile Powder and Crumb Elastomer
- ChevronTexaco Molytex® EP NLGI Grade 0
- DuPont Teijin Films Mylar® LBT-2 Polyester Packaging Film, 48 Gauge
- Dynasol Solprene® 375 Solution Random SBR
- SABIC Innovative Plastics Lexan® SD9705 PC Copolymer (Europe-Africa-Middle East)
- 3M Dyneon™ Aflas® FA-100S PTFE Fluoroelastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved