Toyobo ECOVYLOPET® EMC2310 PET Bottle Recycling Grade, 10% Glass Reinforced

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 10% Glass Reinforced
Manufacturer	Toyobo
Trade Name	ECOVYLOPET®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Toyobo ECOVYLOPET® EMC2310 PET Bottle Recycling Grade, 10% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Features: PET Bottle Recycling Grade, 10% Glass Fiber Reinforced, General PurposeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo.

Physical Properties	Metric	English	Comments
Density	1.59 g/cc	0.0574 lb/in³
Water Absorption	0.060 %	0.060 %	24 hrs at 23°C
Linear Mold Shrinkage, Flow	0.0040 cm/cm @Thickness 2.00 mm	0.0040 in/in @Thickness 0.0787 in
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in

Mechanical Properties	Metric	English
Hardness, Rockwell M	90	90
Tensile Strength at Break	100 MPa	14500 psi
Elongation at Break	2.2 %	2.2 %
Modulus of Elasticity	7.10 GPa	1030 ksi
Flexural Strength	142 MPa	20600 psi
Izod Impact, Notched	0.640 J/cm	1.20 ft-lb/in

Thermal Properties	Metric	English	Comments
CTE, linear	40.0 µm/m-°C @Temperature 20.0 °C	22.2 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	235 °C	455 °F	0.455 MPa
Deflection Temperature at 1.8 MPa (264 psi)	210 °C	410 °F

Processing Properties	Metric	English	Comments
Mold Temperature	110 °C	230 °F