SABIC Innovative Plastics LNP Stat-kon EE006EM PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon EE006EM PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* EE006EM is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive, Easy Molding.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| 1.39 g/cc | 0.0502 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.00080 cm/cm @Time 86400 sec |
0.00080 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.0049 cm/cm @Time 86400 sec |
0.0049 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 194 MPa | 28100 psi | ISO 527 |
| 201 MPa | 29200 psi | ASTM D 638 | |
| Tensile Strength, Yield | 194 MPa | 28100 psi | ISO 527 |
| 201 MPa | 29200 psi | ASTM D 638 | |
| Elongation at Break | 1.3 % | 1.3 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D 638 | |
| Elongation at Yield | 1.2 % | 1.2 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D 638 | |
| Tensile Modulus | 18.79 GPa | 2725 ksi | 1 mm/min; ISO 527 |
| 21.37 GPa | 3099 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 265 MPa | 38400 psi | ISO 178 |
| 268 MPa | 38900 psi | ASTM D 790 | |
| Flexural Modulus | 15.16 GPa | 2199 ksi | ASTM D 790 |
| 15.4 GPa | 2230 ksi | ISO 178 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.69 J/cm @Temperature 23.0 °C |
8.79 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 12.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.67 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 12.6 µm/m-°C @Temperature -40.0 - 40.0 °C |
7.00 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 211 °C @Thickness 3.20 mm |
412 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 206 °C @Thickness 3.20 mm |
403 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- MRC Polymers MAXTELâ„¢ 600T18-UV TPO, 18% Talc Filled, UV Stabilized
- Seals Eastern 5407 Nitrile Rubber
- Teknor Apex Monprene® MP-2328 Thermoplastic Elastomer
- A. Schulman PP 2268-01 Polypropylene High Flow, Impact Copolymer Polypropylene
- DuPont Performance Polymers Delrin® 500TL NC010 Acetal (POM) (Unverified Data**)
- Bedford Plastics Glass Reinforced Vinylester Flat Sheet, 3/8" to 1"
- Asia International Enterprise (Hong Kong) 60C2 Nylon 66
- PolyOne Synprene® RT-3860MS Thermoplastic Elastomer - SBC (discontinued **)
- Rogers Corporation Bisco® L3 Premiere Next Generation Dynamic Flooring Material
- Mitsui MILEX™ RX-2325C Low Silicone Rubber Modified Phenolic Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved