LG Chemical SEETEC BF315 LDPE
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | LG Chemical |
| Trade Name | SEETEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical SEETEC BF315 LDPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: Good Processability and Excellent Optical PropertiesApplications: Masking filmCAS No. 9002-88-4Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 - 0.925 g/cc | 0.921 - 0.925 g/cc | ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.61 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 5.75 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 14.7 MPa | 2130 psi | 500mm/min; ASTM D638 |
| Film Elongation at Break, MD | 300 % | 300 % | 500 mm/min; ASTM D638 |
| Film Elongation at Break, TD | 550 % | 550 % | 500 mm/min; ASTM D638 |
| Elongation at Break | 600 % | 600 % | 500 mm/min; ASTM D638 |
| 2% Secant Modulus | 1.25 GPa | 181 ksi | 500mm/min; ASTM D638 |
| Elmendorf Tear Strength MD | 450 g | 450 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM D1922 |
| Dart Drop Test | 75.0 g | 0.165 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 26.5 MPa | 3840 psi | 500mm/min, Ultimate; ASTM D638 |
| Film Tensile Strength at Break, TD | 24.5 MPa | 3550 psi | 500mm/min, Ultimate; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 105 °C | 221 °F | 10°C/min; ASTM D3418 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 95 % | 95 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CCP20020 UV Polypropylene, Mineral Reinforced, UV stabilized
- Fujipoly Industries Sarcon® 85T Thin-Film TR
- Tra-Con Tra-Bond 2101 General Purpose Epoxy Adhesive
- EMS-Grivory Grivory® L 16 GM nat PA12
- Cytec EN-11 (Conap) Casting, Potting, and Molding Compound
- Arkema Group LOTRYL® 30 BA 02 Copolymer Ethylene - Butyl Acrylate
- Arlon 56344R025 0.025" (0.635 mm) Semi-cured Silicone Rubber
- BASF Neopolen® P 9270 0.09 g/cc Core density; Expanded Polypropylene (Europe)
- Arlon 47568R055E 0.0075" Cured Silicone Rubber/Fiberglass/Acrylic PSA Laminate
- Multibase Multi-ABS 2945 FR Flame Retardant ABS
Copyright © lookpolymers.com All Rights Reserved