SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP Stat-loy
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP STAT-LOY A30009 ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Stat-loy* A30009 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant. Added features of this material include: Antistat, Flame Retardant.

Physical Properties	Metric	English	Comments
Density	1.21 g/cc	0.0437 lb/inÂ³	ASTM D792
	1.21 g/cc	0.0437 lb/inÂ³	ISO 1183
Moisture Absorption	2.30 %	2.30 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0079 cm/cm @Time 86400 sec	0.0079 in/in @Time 24.0 hour	ISO 294
	0.0070 - 0.0090 cm/cm @Time 86400 sec	0.0070 - 0.0090 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.0088 cm/cm @Time 86400 sec	0.0088 in/in @Time 24.0 hour	ISO 294
	0.0080 - 0.010 cm/cm @Time 86400 sec	0.0080 - 0.010 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.0 MPa	3480 psi	ASTM D638
	28.0 MPa	4060 psi	ISO 527
Tensile Strength, Yield	32.0 MPa	4640 psi	ASTM D638
	32.0 MPa	4640 psi	ISO 527
Elongation at Break	15.2 %	15.2 %	ISO 527
	35.8 %	35.8 %	ASTM D638
Elongation at Yield	3.5 %	3.5 %	ISO 527
	3.8 %	3.8 %	ASTM D638
Tensile Modulus	1.72 GPa	249 ksi	1 mm/min; ISO 527
	2.06 GPa	299 ksi	50 mm/min; ASTM D638
Flexural Strength	41.0 MPa	5950 psi	ASTM D790
	47.0 MPa	6820 psi	ISO 178
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
	2.06 GPa	299 ksi	ASTM D790
Izod Impact, Notched	1.33 J/cm	2.49 ft-lb/in	ASTM D256
Izod Impact, Unnotched	16.98 J/cm	31.81 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/mÂ²	5.23 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	141 kJ/mÂ²	67.1 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	14.0 J	10.3 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	4.00 J	2.95 ft-lb	Multiaxial Impact; ISO 6603

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	114 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	63.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	115 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	63.9 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	95.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	52.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
	95.4 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	53.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi)	94.0 Â°C	201 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	95.0 Â°C @Thickness 3.20 mm	203 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	81.0 Â°C	178 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	81.0 Â°C @Thickness 3.20 mm	178 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Surface Resistance	1.00e+9 - 1.00e+11 ohm	1.00e+9 - 1.00e+11 ohm	ASTM D257