DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® HTR8223 BK320 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
42 Shore D High Viscosity Polyester Elastomer Developed for Blow MoldingInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.00 g/cc
0.0361 lb/in³
1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 0.80 %

@Thickness 2.00 mm
 0.80 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
Immersion 24h; ASTM D570
Viscosity 135000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 135000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
540000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 540000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
2.60e+6 cP

@Shear Rate 10.0 1/s,
Temperature 230 °C
 2.60e+6 cP

@Shear Rate 10.0 1/s,
Temperature 446 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Melt Flow 9.5 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 9.5 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 ISO 1133
10 g/10 min

@Load 10.0 kg,
Temperature 230 °C
 10 g/10 min

@Load 22.0 lb,
Temperature 446 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 38
38
15s; ISO 868
<= 42
<= 42
ISO 868
Tensile Strength at Break 26.0 MPa
3770 psi
ISO 527-1/-2
Tensile Stress 3.50 MPa

@Strain 5.00 %
 508 psi

@Strain 5.00 %
 ISO 527-1/-2
5.50 MPa

@Strain 10.0 %
 798 psi

@Strain 10.0 %
 ISO 527-1/-2
10.0 MPa

@Strain 50.0 %
 1450 psi

@Strain 50.0 %
 ISO 527-1/-2
13.0 MPa

@Strain 100 %
 1890 psi

@Strain 100 %
 ISO 527-1/-2
19.0 MPa

@Strain 300 %
 2760 psi

@Strain 300 %
 ISO 527-1/-2
0.590 MPa

@Strain 0.230 %,
Temperature -40.0 °C
 85.6 psi

@Strain 0.230 %,
Temperature -40.0 °F
 TPE; ISO 11403-1 -2
0.800 MPa

@Strain 2.10 %,
Temperature 150 °C
 116 psi

@Strain 2.10 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
1.63 MPa

@Strain 3.43 %,
Temperature 120 °C
 236 psi

@Strain 3.43 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
2.09 MPa

@Strain 9.54 %,
Temperature 150 °C
 303 psi

@Strain 9.54 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
2.49 MPa

@Strain 5.06 %,
Temperature 90.0 °C
 361 psi

@Strain 5.06 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
2.70 MPa

@Strain 17.6 %,
Temperature 150 °C
 392 psi

@Strain 17.6 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.05 MPa

@Strain 26.28 %,
Temperature 150 °C
 442 psi

@Strain 26.28 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.27 MPa

@Strain 35.21 %,
Temperature 150 °C
 474 psi

@Strain 35.21 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.49 MPa

@Strain 47.26 %,
Temperature 150 °C
 506 psi

@Strain 47.26 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.66 MPa

@Strain 59.34 %,
Temperature 150 °C
 531 psi

@Strain 59.34 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.67 MPa

@Strain 14.49 %,
Temperature 120 °C
 532 psi

@Strain 14.49 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
3.80 MPa

@Strain 71.13 %,
Temperature 150 °C
 551 psi

@Strain 71.13 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
3.94 MPa

@Strain 82.6 %,
Temperature 150 °C
 571 psi

@Strain 82.6 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.14 MPa

@Strain 98.83 %,
Temperature 150 °C
 600 psi

@Strain 98.83 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.28 MPa

@Strain 109.17 %,
Temperature 150 °C
 621 psi

@Strain 109.17 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.44 MPa

@Strain 121.65 %,
Temperature 150 °C
 644 psi

@Strain 121.65 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
4.57 MPa

@Strain 26.51 %,
Temperature 120 °C
 663 psi

@Strain 26.51 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
4.66 MPa

@Strain 138.08 %,
Temperature 150 °C
 676 psi

@Strain 138.08 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.10 MPa

@Strain 38.95 %,
Temperature 120 °C
 740 psi

@Strain 38.95 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.48 MPa

@Strain 22.21 %,
Temperature 90.0 °C
 795 psi

@Strain 22.21 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
5.49 MPa

@Strain 51.4 %,
Temperature 120 °C
 796 psi

@Strain 51.4 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
5.50 MPa

@Strain 13.54 %,
Temperature 60.0 °C
 798 psi

@Strain 13.54 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
5.93 MPa

@Strain 67.6 %,
Temperature 120 °C
 860 psi

@Strain 67.6 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.32 MPa

@Strain 82.83 %,
Temperature 120 °C
 917 psi

@Strain 82.83 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.50 MPa

@Strain 41.29 %,
Temperature 90.0 °C
 943 psi

@Strain 41.29 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
6.69 MPa

@Strain 97.45 %,
Temperature 120 °C
 970 psi

@Strain 97.45 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.03 MPa

@Strain 111.25 %,
Temperature 120 °C
 1020 psi

@Strain 111.25 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.08 MPa

@Strain 15.55 %,
Temperature 40.0 °C
 1030 psi

@Strain 15.55 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
7.09 MPa

@Strain 60.93 %,
Temperature 90.0 °C
 1030 psi

@Strain 60.93 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.53 MPa

@Strain 130.82 %,
Temperature 120 °C
 1090 psi

@Strain 130.82 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
7.57 MPa

@Strain 80.16 %,
Temperature 90.0 °C
 1100 psi

@Strain 80.16 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.82 MPa

@Strain 37.99 %,
Temperature 60.0 °C
 1130 psi

@Strain 37.99 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
7.83 MPa

@Strain 142.91 %,
Temperature 120 °C
 1140 psi

@Strain 142.91 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.00 MPa

@Strain 14.96 %,
Temperature 23.0 °C
 1160 psi

@Strain 14.96 %,
Temperature 73.4 °F
 TPE; ISO 11403-1 -2
8.17 MPa

@Strain 104.16 %,
Temperature 90.0 °C
 1180 psi

@Strain 104.16 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.20 MPa

@Strain 157.24 %,
Temperature 120 °C
 1190 psi

@Strain 157.24 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.66 MPa

@Strain 9.79 %,
Temperature -20.0 °C
 1260 psi

@Strain 9.79 %,
Temperature -4.00 °F
 TPE; ISO 11403-1 -2
8.69 MPa

@Strain 175.85 %,
Temperature 120 °C
 1260 psi

@Strain 175.85 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.74 MPa

@Strain 126.26 %,
Temperature 90.0 °C
 1270 psi

@Strain 126.26 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
8.76 MPa

@Strain 64.0 %,
Temperature 60.0 °C
 1270 psi

@Strain 64.0 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
9.20 MPa

@Strain 195.71 %,
Temperature 120 °C
 1330 psi

@Strain 195.71 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.27 MPa

@Strain 146.52 %,
Temperature 90.0 °C
 1340 psi

@Strain 146.52 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
9.52 MPa

@Strain 88.68 %,
Temperature 60.0 °C
 1380 psi

@Strain 88.68 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
9.54 MPa

@Strain 44.98 %,
Temperature 40.0 °C
 1380 psi

@Strain 44.98 %,
Temperature 104 °F
 TPE; ISO 11403-1 -2
9.64 MPa

@Strain 15.8 %,
Temperature 0.000 °C
 1400 psi

@Strain 15.8 %,
Temperature 32.0 °F
 TPE; ISO 11403-1 -2
9.77 MPa

@Strain 165.32 %,
Temperature 90.0 °C
 1420 psi

@Strain 165.32 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2